 VC-FILM type
VC-FILM consists of alternate layers of conductive and insulating silicone rubber and of rubber insulators with less stiffness, which are fitted on both sides. This type is suitable for small- or middle-sized displays.
While VC FILM type has translucent supportive solid rubber on the both sides, SG type has pink sponge rubber.

Usage Example of VC-Film

Outline Dimensions:

Chemical Resistance:
Chemical
Solvent
Light Transmittance
(Before soaking)
Light Transmittance
(After soaking)
Appearance
change
 Methanol 78.0% 78.0% None
 Ethanol 77.9% 77.9%
 Neutral Detergent 77.8% 77.7%
 Leather wax 77.9% 78.7%
 Engine oil 77.9% 78.2%
 Chocolate 78.0% 78.1%
 Regular gasoline 77.6% 76.8% Slightly swollen at edge
 Special gasoline 77.8% 76.6%
General Characteristics:
Characteristics Item Characteristic value Unit Test method
 Thermal characteristics Deflection temperature 126.8 °C JIS- K- 7207
Linear expansion coefficient 8.0 10-5mm/mm/°C ASTM- D- 696
Heat shrinkage TD 0.15 % JIS- K- 6735
MD 0.10 % JIS- K- 6735
Flammability SE class - FMVSS- 302
 Mechanical characteristics Tensile strength 300 kg/cm² JIS- K- 7113
Elongation 110 % JIS- K- 7113
Peel strength 1.3 kg/25mm JIS- K- 6854
 Optical characteristics Light transmittance 78 % JIS- K- 7105
*FMVSS:Federal Motor Vehicle Safety Standards
Note: VC 908500 has been used as a test Sample.
Environment-proof Characteristics:
Test item Test condition Peeling Color change Dimensional Change Warp
 High-temperature test 85°C(1000hrs) None None -0.03 % None
120°C(240hrs) None -0.04 %
 Low-temperature test -40°C(240hrs) None None
 Higt-temperature/higt-humidity test 60°C,95%RH(240hrs) None +0.02 %
80°C,95%RH(240hrs) None -0.02 %
 Weatherabillity test 240hrs None -
480hrs Slight color change -
 Thermal shock -40°C(1hr)?`85°C(1hr)×100cycles None -0.02 %
 Heat cycle 85°C(2hrs)-
Room temperature(2hrs)
-40°C(2hrs)-Room temperature
(2hrs)×20cycles
6 -0.02 %
Note:
  1. VC 908300 used as a test Sample.
  2. Sample size 100?~20mm(100mm in the louver axial direction).
  3. Warp of the sample, placed on the aluminum place, was measured using a clearance gauge.
  4. The sunshine-type wearher mecer was used for the wearhecability rest with black panel rempecature of 63 deg.
VC-FILM Standard Grad:
TYPE Visible angle Louver angle Max. light transmittance angle Tickness Outer dimension
 VC- 128500 120 ° 0 ° 0 ° 0.9 260×300
 VC- 128510 10 ° 11 °
 VC- 128518 18 ° 23 °
 VC- 908500 90 ° 0 ° 0 ° 0.9
 VC- 908510 10 ° 11 °
 VC- 908518 18 ° 23 °
 VC- 609500 60 ° 0 ° 0 ° 1.0
 VC- 609510 10 ° 11 °
 VC- 609518 18 ° 23 °

Usage Example of Mobile Phone Usage Example of VC-Film Shin-Etsu Polymer America, Inc. Company Information Shin-Etsu Polymer Green Activities